Crystaline Powder 20 / 25kg Poly lined poly woven bag / Poly lined paper bag. It is white or yellow crystalline. It can be dissolved in acetone, benzene, toluene, ethyl ether and ethyl acetate as well as warm carbon tetra chloride, ethyl alcohol and heptane. It also can be slightly dissolved in gasoline, but not in kerosene and water.
PVI is an effective scorch inhibitor with almost all types of accelerators and in all types of sulphur cured diene rubber based compounds.
Crystaline Powder
PVI is an ideal pre vulcanization (scorch) inhibitor for NR, IR, NR-BR blend, SBR, NR-SBR, SBR-BR blends, NBR, CR and other diene rubber based accelerated sulphur cured compounds.
The product may be used in natural rubber and synthetic rubber. It may protect effectively the rubber material from scorching during Processing, So that to make it possible for extruder and calender to be running at a high temperature and high speed and improve the production capacity of vulcanizer. The product also can improve the storage stabilization of the rubber material, protect natural vulcanization during storage. It has reclaimaion function for rubber material, which bearing high heating or with dangers of scorching.
PVI can be used effectively in compounds based on NBR/PVC blends, polyacrylic rubbers and sulphur cured polyurethanes.
PVI is most effective at sulphur dosages between 1.5-3.0 phr and it is not effective with organic peroxide, PF resin and metal oxide cure
PVI does not cause any detrimental effect on the vulcanizate properties such as tensile strength, modulus values, and resilience / heat build up, compression set or permanent set, ozone resistance and hot air aged vulcanizate properties when used at optimum dosage.
PVI does not cause contact or migration staining but can slightly discolor bright white rubber products.
PVI can permit addition of curatives at an early stage of mixing for better dispersion of curatives, reduced mixing cycle time, reduced power consumption, reduced labor and capital investment costs.
PVI use of higher processing speeds and temperatures during mixing, calendaring, extrusion, etc. for increased productivity and reduced processing cost.
PVI use of higher injection temperatures and shorter cure cycles for increased productivity.
PVI recovery of rubber compounds with marginal processing safety and recovery of partially scorched compound for scrap elimination.
PVI improve the storage stability of fully compounded stocks at ambient temperatures.
Composition Specification: N-(Cyclohexylthio) phthalimide
Melting Point : 90-95 Degree C
|
Item |
Specification |
|
Appearance |
White or Light yellow powdered crystal |
|
Available composition content |
96% Min. |
|
Melting point |
89 -94°C |
|
Heating loss |
0.50% Max |
|
Ash content |
0.10% Max |
|
Residue(150um) |
0.0% Max |
|
Identification IR |
Identical to standard |
Chemical name: N-(cyclhexyl thio) phthalimide
Molecular Formula: C14H15O2NS
PVI ANTISCORCHING Rubber Chemicals manufacturer supplier distributor in Mumbai, Kandla, Kolkata, Vizag, Chennai, India, Fujairah, Dubai, Sharjah, UAE, Gulf, Middle East, Muscat Oman, Kenya Africa. Get the best quality of PVI ANTISCORCHING Rubber Chemicals at a competitive price from us. We have ready stock of PVI ANTISCORCHING Rubber Chemicals in India, UAE Gulf, Oman, Kenya Africa. Contact us for bulk as well as small orders.